KetaSpire® KT-880FP

聚醚醚酮

Solvay Specialty Polymers

Technical Data

 

产品说明

KetaSpire® KT-880FP is the high-flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural color fine powder form for compression molding and other uses that can benefit from the fine powder form.

 

KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases.

 

These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses.

 

The resin is also available as KetaSpire KT-880 NT in a natural-color pellet form for injection molding.

 

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  Solvay Specialty Polymers

•  KetaSpire®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

• 尺寸稳定性良好 • 抗伽马辐射 • 热消毒

• 电子束消毒 • 良好抗撞击性

• 放射性可透的 • 流动性高 • 生物兼容性

特性 • 辐射消毒 • 耐化学品性能，良好 • 延展性

• 高压锅消毒 • 耐疲劳性能 • 用蒸汽消毒

• 好的消毒性 • 耐热性，高 • 阻燃性

• 环氧乙烷消毒 • 耐蒸汽

• 薄膜 • 连接器 • 医疗/护理用品

• 泵件 • 密封件

用途 • 电气/电子应用领域 • 石油/天然气用品 • 医疗器材

• 飞机应用 • 外科器械 • 医疗器械

• 工业应用 • 牙齿应用领域

机构评级 • ISO 10993 • ISO 10993-第一部分

RoHS 合规性 • RoHS 合规

外观 • 黑色 • 自然色

形式 • 粒子 2

• 薄膜挤出 • 挤出吹塑成型 • 型材挤出成型

加工方法 • 电线&线缆挤出成型 • 热成型

• 注射成型

• 机器加工 • 纤维（纺纱）挤出

物理性能 额定值单位制 测试方法

密度 / 比重 1.30g/cm³ ASTM D792

熔流率（熔体流动速率） (400°C/2.16 kg) 36g/10 min ASTM D1238

收缩率 4 ASTM D955

流动 : 0.318 mm 1.4 到 1.6%

横向流动 : 3.18 mm 1.5 到 1.7%

吸水率 (24 hr) 0.10% ASTM D570

颗粒大小 - D50 30.0 到 45.0µm

机械性能 额定值单位制 测试方法

拉伸模量

-- 5 3700MPa ASTM D638

-- 4000MPa ISO 527-1/1A/1

拉伸应力

屈服 102MPa ISO 527-2/1A/50

-- 6 100MPa ASTM D638

 

KetaSpire® KT-880FP

聚醚醚酮

Solvay Specialty Polymers

机械性能 额定值单位制 测试方法

伸长率

屈服 7 5.2% ASTM D638

屈服 5.0% ISO 527-2/1A/50

断裂 7 10 到 20% ASTM D638

断裂 10 到 20% ISO 527-2/1A/50

弯曲模量

-- 3800MPa ASTM D790

-- 3900MPa ISO 178

弯曲强度

-- 153MPa ASTM D790

-- 134MPa ISO 178

压缩强度 123MPa ASTM D695

剪切强度 95.1MPa ASTM D732

泊松比 0.37 ASTM E132

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度

-- 53J/m ASTM D256

-- 4.9kJ/m² ISO 180

无缺口悬臂梁冲击 无断裂 ASTM D4812

ISO 180

硬度 额定值单位制 测试方法

洛氏硬度 (M 级) 102 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 (1.8 MPa, 已退火) 160°C ASTM D648

玻璃转化温度 147°C ASTM D3418

熔融峰值温度 343°C ASTM D3418

线形热膨胀系数 - 流动 (-50 到 50°C) 5.0E-5cm/cm/°C ASTM E831

比热 DSC

50°C 1330J/kg/°C

200°C 1930J/kg/°C

导热系数 0.25W/m/K ASTM E1530

电气性能 额定值单位制 测试方法

表面电阻率 > 1.9E+17ohms ASTM D257

体积电阻率 3.8E+17ohms•cm ASTM D257

介电强度 (3.00 mm) 15kV/mm ASTM D149

介电常数 ASTM D150

60 Hz 3.10

1 kHz 3.01

1 MHz 3.07

耗散因数 ASTM D150

60 Hz 1.0E-3

1 kHz 1.0E-3

1 MHz 3.0E-3

充模分析 额定值单位制 测试方法

熔体粘度 (400°C, 1000 sec^-1) 150Pa•s ASTM D3835

补充信息

The particle size distribution is such that no particle is larger than 149 microns, and less than 2% of the weight of the material is larger than 106 microns.

 

KetaSpire® KT-880FP

聚醚醚酮

Solvay Specialty Polymers

注射 额定值单位制

干燥温度 150°C

干燥时间 4.0hr

料筒后部温度 355°C

料筒中部温度 365°C

料筒前部温度 370°C

射嘴温度 375°C

模具温度 175 到 205°C

注射速度 快速

螺杆压缩比 2.5:1.0 到 3.5:1.0

 

 

 

 

生物兼容三类医疗ISO 10993聚醚醚酮,生物兼容三类医疗ISO 10993 PEEK KetaSpire® KT-880FP是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581