玻璃纤维增强材料35%,良好的流动性, 耐化学性良好, 吸潮性差, 金属置换, 连接器, 阀门/阀门部件

 

Amodel® A-6135 HN

聚二甲苯酰胺

Solvay Specialty Polymers

Technical Data

 

产品说明

 

Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties.

 

Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units.

 

• Black: A-6135 HN BK 324

• Natural A-6135 HS NT

总体

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

搜索 UL 黄卡 •  Solvay Specialty Polymers

•  Amodel®

供货地区 • 北美洲 • 南美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料, 35% 填料按重量

添加剂 • 热稳定剂

• 刚性，高 • 良好的流动性 • 透湿性强

性能特点 • 刚性，良好 • 耐化学性良好

• 高强度 • 耐热性，高 • 吸潮性差

• 良好的抗蠕变性 • 热稳定性

• Electrical Housing • 工业领域： • 汽车电子

• 草坪和园林设备 • 工业配件 • 汽车领域的应用：

用途 • 电气/电子应用领域 • 金属置换 • 设备/机械部件

• 动力/其它工具 • 连接器 • 型号

• 阀门/阀门部件 • 汽车的发动机罩下的零件 • 一般目的

RoHS 合规性 • 联系制造商

外观 • 黑色

形式 • 颗粒料

加工方法 • Water-Heated Mold Injection Molding

多点数据 • Isothermal Stress vs. Strain (ISO 11403-1)

 

物理性能 干燥 调节后的 单位制 测试方法

密度 1.45 -- g/cm³ ISO 1183/A

收缩率

流动 0.60 -- % ASTM D955

横向流动 0.90 -- % ASTM D955

横向流量 1.0 -- % ISO 294-4

流量 0.50 -- % ISO 294-4

吸水率

24 hr 0.30 -- % ASTM D570

23°C, 24 hr 0.29 -- % ISO 62

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量

-- 13800 12200 MPa ASTM D638

23°C 11500 -- MPa ISO 527-2

100°C 7310 -- MPa ISO 527-2

150°C 6270 -- MPa ISO 527-2

175°C 5310 -- MPa ISO 527-2

 

Amodel® A-6135 HN

聚二甲苯酰胺

Solvay Specialty Polymers

机械性能 干燥 调节后的 单位制 测试方法

拉伸应力

断裂, 23°C 211 -- MPa ISO 527-2

断裂, 100°C 121 -- MPa ISO 527-2

断裂, 150°C 92.4 -- MPa ISO 527-2

断裂, 175°C 82.0 -- MPa ISO 527-2

-- 203 176 MPa ASTM D638

伸长率

断裂 1.9 2.1 % ASTM D638

断裂, 23°C 2.0 -- % ISO 527-2

断裂, 100°C 4.3 -- % ISO 527-2

断裂, 150°C 4.9 -- % ISO 527-2

断裂, 175°C 4.7 -- % ISO 527-2

弯曲模量

-- 11400 11000 MPa ASTM D790

23°C 11400 -- MPa ISO 178

100°C 6600 -- MPa ISO 178

150°C 4900 -- MPa ISO 178

175°C 4600 -- MPa ISO 178

弯曲强度

-- 310 249 MPa ASTM D790

3.5% 应变, 23°C 300 -- MPa ISO 178

3.5% 应变, 100°C 170 -- MPa ISO 178

3.5% 应变, 150°C 123 -- MPa ISO 178

3.5% 应变, 175°C 112 -- MPa ISO 178

压缩强度 148 -- MPa ASTM D695

剪切强度 87.6 73.8 MPa ASTM D732

泊松比 0.39 -- ASTM E132

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 (23°C) 9.2 -- kJ/m² ISO 179/1eA

简支梁缺口冲击强度 (23°C) 60 -- kJ/m² ISO 179/1eU

悬壁梁缺口冲击强度

-- 85 69 J/m ASTM D256

23°C 9.1 -- kJ/m² ISO 180

无缺口悬臂梁冲击

-- 800 -- J/m ASTM D256

23°C 62 -- kJ/m² ISO 180

硬度 干燥 调节后的 单位制 测试方法

洛氏硬度 (R 计秤) 125 -- ASTM D785

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 303 -- °C ISO 75-2/B

1.8 MPa, 未退火 288 -- °C ISO 75-2/A

1.8 MPa, 退火, 3.20 mm 291 -- °C ASTM D648

熔融温度 310 -- °C ASTM D570

ISO 11357-3

线形膨胀系数 ASTM E831

流动 : 0 到 100°C 0.000022 -- cm/cm/°C

流动 : 100 到 200°C 0.000016 -- cm/cm/°C

横向 : 0 到 100°C 0.000061 -- cm/cm/°C

横向 : 100 到 200°C 0.00010 -- cm/cm/°C

注射 干燥单位制

干燥温度 120°C

干燥时间 4.0hr

 

Amodel® A-6135 HN

聚二甲苯酰胺

Solvay Specialty Polymers

注射 干燥单位制

建议的最大水分含量 0.045%

螺筒后部温度 316 到 321°C

螺筒前部温度 327 到 332°C

加工（熔体）温度 321 到 335°C

模具温度 65.6 到 93.3°C

注射说明

Injection Rate: 3 to 6 in/sec

Holding Pressure: 50% of injection pressure

 

 

 

 

 